Determination of K2O in High Potassium Aluminosilicate by Tetraphenylborate Gravimetry
-
摘要: 为了精确测定分解反应过程中钾的挥发量, 结合GB8574-2002, 在样品高钾铝硅酸盐物料(钾长石、碳酸钾焙烧熟料, K2O含量大于15%)处理中采用聚环氧乙烷絮凝沉淀Si, 新制Ca(OH)2溶液除去Mg2+、Fe2+、Fe3+、Mn2+等其他阳离子, 加入碳酸铵稳定溶液pH值以除去Ca2+和Al3+.采用四苯硼钾重量法测定钾含量, 测定结果与表样对照, 相对误差在0.5%以内.实验表明: 利用Ca(OH)2除杂, 溶液pH值须控制在10~ 12;碳酸铵双水解反应后, 溶液pH值须控制在7.35左右以除尽Ca2+和Al3+; 低温(T < 473 K)蒸发溶液除去NH4+, 消除了因生成四苯硼铵沉淀而带来的分析误差.结果表明该方法可以精确测定高钾铝硅酸盐物料的K2O含量, 具有成本低、方便快捷、无需大型仪器之优点.Abstract: A convenient and rapid method was established to determine K2O content in high potassium aluminosilicate(K2O content> 15%), which was obtained by calcining K-feldspar and K2CO3. Combined with the GB8574-2002 potassium tetraphenylborate gravimetry method, silicon was deposited by polyethylene oxide in an acid environment. Other cations such as Mg2+, Fe3+, Fe2+, Mn2+ were removed by the intrusion of newly formed calcium hydroxide solution by controlling pH at 10-12. The remaining Al3+ and Ca2+ were eliminated by salvolatile hydrolyzation which stabilized the solution at about pH = 7.35. Before the potassium tetraphenylborate gravimetry method, the introduced ammonia was removed by low temperature(T < 473 K)calcining to avert ammonium tetraphenylborate precipitation. The relative error in this experiment was less than 0.5% by comparison with standard specimen.
-
图 1 25 ℃离子形态分布随pH值的变化
Fig. 1. Distribution of aqueous species as a function of pH in 25 ℃
表 1 溶液pH值对测定结果的影响
Table 1. pH value influence on test
表 2 样品的化学全分析结果
Table 2. Chemical composition of samples
表 3 本文测试结果Ⅰ与标准试样Ⅱ比较
Table 3. Analysis result and comparison with standard sample
-
Chemical Analysis Lab Group of China University of Geosciences(Beijing), 1990. Silicate rock and mineral analysis. 1st Edition. Geological Publishing House, Beijing, 204-209(in Chinese). Li, L. Q., Lin, C.S., Jiang, W. Q., et al., 1997. Quantity analysis chemistry. University of Science and Technology of China Press, Hefei, 90-93(in Chinese). Liu, J.G., Wang, Y.X., 1994. Coagulating agent for gravimetric determination of silica in rocks and minerals. Rocks and Minerals Analysis, 13(2): 134-136(in Chinese with English abstract). Luo, X.J., Yang, W.D., Li, R.X., et al., 2001. Effect of pH on the solubility of the feldspar and the development of secondary porosity. Bulletin of Mineralogy, Petrology and Geochemistry, 20(2): 103-107(in Chinese with English abstract). Si, X.B., Gao, Y.L., 2002. Development on potassium tetraphenylborate gravimetry. Anhui Chemical Engineering, (4): 46-47(in Chinese with English abstract). Zhang, X.H., Ma, H.W., Yang, J., et al., 2003. An experimental synthesis of 13X zeolite molecular sieves from potassium feldspar powder with high content ratio of Fe2O3. Acta Petrologica et Mineralogica, 22(2): 167-172(in Chinese with English abstract). 李龙泉, 林长山, 江万权, 等, 1997. 定量分析化学. 合肥: 中国科学技术大学出版社, 90-93. 刘建国, 王粤新, 1994. 重量法测定岩石矿物中二氧化硅的几种凝聚剂. 岩矿测试, 113(2): 134-136. https://www.cnki.com.cn/Article/CJFDTOTAL-YKCS402.012.htm 罗孝俊, 杨卫东, 李荣西, 等, 2001. pH值对长石溶解度及次生孔隙发育的影响. 矿物岩石地球化学通报, 20(2): 103-107. doi: 10.3969/j.issn.1007-2802.2001.02.007 司学兵, 高云龙, 2002. 四苯硼酸钠重量法测钾含量方法的改进. 安徽化工, (4): 46-47. doi: 10.3969/j.issn.1008-553X.2002.04.021 章西焕, 马鸿文, 杨静, 等, 2003. 利用高铁钾长石粉水热合成13X沸石分子筛的实验研究. 岩石矿物杂志, 22(2): 167-172. https://www.cnki.com.cn/Article/CJFDTOTAL-YSKW200302011.htm 中国地质大学(北京)化学分析室, 1990. 硅酸盐岩石和矿物分析(第一版). 北京: 地质出版社, 204-209. -
下载:
点击查看大图
图(1) / 表(3)
计量
- 文章访问数: 3666
- HTML全文浏览量: 350
- PDF下载量: 7
- 被引次数: 0